Modification of hexagonal boron nitride nanoparticles with fluorosilane
CERAMICS INTERNATIONAL, cilt.42, sa.5, ss.6312-6318, 2016 (SCI-Expanded, Scopus)
- Yayın Türü: Makale / Tam Makale
- Cilt numarası: 42 Sayı: 5
- Basım Tarihi: 2016
- Doi Numarası: 10.1016/j.ceramint.2016.01.019
- Dergi Adı: CERAMICS INTERNATIONAL
- Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
- Sayfa Sayıları: ss.6312-6318
- Anahtar Kelimeler: Hexagonal boron nitride, Functionalization, Fluorosilane, Nanoparticle, CARBOTHERMIC FORMATION, SURFACE MODIFICATION, SILANE, FUNCTIONALIZATION, CARBONATE, COATINGS
- Akdeniz Üniversitesi Adresli: Evet
Özet
Surfaces of hexagonal boron nitride (hBN) nanoparticles were modified with perfluorooctyl-triethoxysllane (FTS). Experiments were performed for 40-120 min in 70-150 degrees C range with FTS/hBN weight ratio in the range of 0.5-1.5. The products were analyzed by FT-IR, TGA, FESEM, HRTEM and EDX. Results of FT-IR analyses indicated that modification takes place in 80 min at 150 degrees C under reflux with a FTS/hBN ratio of 1.5. Presence of FTS on hBN nanoparticles was confirmed by the weight losses in TGA, and by TEM, TEM-EDX analyses. (C) 2016 Elsevier Ltd and Techna Group S.r.l. All rights reserved.