Microstructure and magnetoresistance of a La0.67Ca0.33MnO3 film produced using the dip-coating method

Gunes M., GENÇER H., KOLAT V. S., Vural S., Mutlu H., SEÇKİN T., ...Daha Fazla

Materials Science and Engineering: B, cilt.136, sa.1, ss.41-45, 2007 (SCI-Expanded) identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 136 Sayı: 1
  • Basım Tarihi: 2007
  • Doi Numarası: 10.1016/j.mseb.2006.08.052
  • Dergi Adı: Materials Science and Engineering: B
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.41-45
  • Anahtar Kelimeler: Colossal magnetoresistance, Dip-coating, Manganites, Thick film
  • Akdeniz Üniversitesi Adresli: Hayır

Özet

The microstructure and magnetoresistance properties of polycrystalline bulk La0.67Ca0.33MnO3 and a La0.67Ca0.33MnO3 film produced on a LaAlO3 (1 0 0) single-crystal substrate using the dip-coating method were investigated. X-ray powder diffraction indicated that both film and bulk samples have perovskite structure. Scanning electron microscope and X-ray results clearly indicated that a La0.67Ca0.33MnO3 film was successfully produced using the dip-coating process. This film showed a metal-insulator transition at 269 K and a maximum magnetoresistance ratio (MR (%)) of 56% at 269 K and 6 T magnetic field. © 2006 Elsevier B.V. All rights reserved.